Potential carriers of chemotherapeutic drugs: matrix based nanoparticulate polymeric systems


In this work matrix based nanoparticulate polymer systems have been designed using the diacrylate derivative of the well-known biocompatible polymer, poly(ethylene glycol) (PEG). This has been crosslinked using bifunctional (ethyleneglycol dimethacrylate) and tetrafunctional (pentaerythritol tetraacrylate) crosslinkers in varied concentrations (10-90%) to result in a polymeric network. The crosslinked polymers thus obtained were characterized by spectroscopic techniques (NMR and FTIR) and then prepared nanoparticles by the nanoprecipitation technique. Particle size analysis showed sizes of ~150 nm (PDI < 1) (with tetrafunctional crosslinker) and ~300 nm (with bifunctional crosslinker). Both the systems however showed unimodal narrow particle size distributions with negative zeta potential values of -15.6 and -7.3 respectively. Cytotoxicity of these formulations was evaluated by MTT assay showing non-cytotoxic nature of these carrier systems. In vitro drug loading and release studies were carried out using a model chemotherapeutic drug, methotrexate(MTX). These MTX loaded nanoformulations have also been evaluated biologically with the help of in vivo studies using radiolabeling techniques (with 99mTc radionuclide). The blood kinetics profile of the formulations was studied on New Zealand Albino rabbits while the biodistribution studies were performed on balb/c mice (with EAT tumours), which revealed a hepatobiliary mode of elimination. These preliminary studies clearly demonstrated the ability of these multifunctional crosslinkers to result in tight nanosized networks with biocompatible polymers such as PEG and their potential to carry chemotherapeutic drugs.


The past few decades have seen a tremendous advancement in the area of drug delivery using polymeric particulate carrier systems for small and large molecules. Enhanced medical treatments do not always require a stronger medicine/drug but a better mechanism to deliver the drug. Crosslinked polymeric systems have shown much interest owing to their potential applications for the entrapment and release of multitude of pharmaceutically active molecules and drugs [[1]]. Nanoparticulate systems are a great platform to alter and thereby help to improve the pharmacokinetic and pharmacodynamic properties of various types of drug molecules [[2]–[4]].

Matrix based nanoparticulate polymeric systems offer unique advantages for polymer based drug delivery systems (DDS) over polymer–protein conjugates [[5]], polymer–drug conjugates [[6],[7]], micelles [[8]–[10]], and vesicles [[11]] based on amphiphilic and doubly hydrophilic block copolymers [[12],[13],[33]], dendrimers [[15],[16]], and submicron-sized particulates [[17]]. These offer tunable sizes from nanometers to several micrometers and a large surface area for multivalent bioconjugation. They also have an interior network for the incorporation of therapeutics such as drugs, proteins, etc. Polymeric networks with physically entrapped bioactive molecules such as drugs, proteins, carbohydrates and DNA have been extensively investigated as targeted drug delivery carriers for biomedical applications [[18]]. Crosslinked polymeric systems can be prepared by chemical crosslinking of the polymeric matrices in the presence of various crosslinkers such as ethyleneglycol dimethacrylate (EGDMA), polycaprolactone (PCL) diacrylate, methyl methacrylate (MMA), divinyl benzene (DVB), pentaerythritol triacrylate (PETA), pentaerythritol tetraacrylate, etc. The crosslinking agents play a pivotal role in the preparation of nanoparticulate systems since various properties such as size, shape, structure, etc. depend on the type and concentration of the crosslinker used in the system. Such crosslinked systems show higher stability for prolonged circulation in the bloodstream owing to their chemically crosslinked structure. Their interior network acts as a drug reservoir providing enhanced drug loading by physical entrapment relative to non-crosslinked systems. The entrapment efficiency can be further enhanced by varying the crosslink density which is determined by the number of crosslinks governed by the type of crosslinker used for the preparation of the network. Drug encapsulation in these crosslinked polymeric systems such as PEG based systems could be tailored by several parameters, viz.-a-viz. the functionality of the crosslinker, the molecular weight of the PEG derivative and the architecture of the PEG molecule (linear versus star shaped PEG derivative). The improved drug loading efficiency of these systems augments the bioavailability of the drug thereby reducing any undesired side effects [[19]]. This is undeniably a highly advantageous aspect while using anti-cancer drugs as their side effects may result in compromised efficacy. Both biodegradable and biocompatible polymers have been investigated to prepare crosslinked networks that can carry chemotherapeutic drug payloads for therapeutic and delivery purposes. Cytarabine encapsulated chitosan nanoparticles using sodium tripolyphosphate as a crosslinking agent have been prepared that showed controlled release over a period of time [[20],[21]]. Core-shell crosslinked nanoparticles, having polycaprolactone core and polyethyleneglycol or poly [2-(N,N-dimethylamine) ethyl methacrylate] shells have been investigated to encapsulate cisplatin and show cytostatic efficacies against a human ovarian adenocarcinoma cell line [[22],[23]]. Extensive research has been done utilizing poly(ethylene glycol)(PEG) for drug delivery applications owing to its biocompatible nature. Cross-linked PEGs are finding increasing application as carriers of chemotherapeutic agents be it in the form of hydrogels [[30],[31]] or in the form of copolymer micelles [[32],[14],[34]]. It was therefore proposed to use PEG as the core polymer for our work in order to further exploit its favorable attributes.

In this work we describe the synthesis and characterization of crosslinked PEG based nanoparticles and explore their potential to be used as drug delivery carriers. We used the acrylated derivative of polyethyleneglycol, i.e. polyethyleneglycol diacrylate(PEGDA) as the main polymer and crosslinked it using bifunctional and tetra functional crosslinkers, ethyleneglycoldimethacrylate (EGDMA) and pentaerythritol tetraacrylate (PETRA) respectively. The prepared nanoparticles were characterized by physico-chemical characterization techniques such as NMR, FTIR, dynamic light scattering (DLS) and Zeta potential measurements. These were loaded with methotrexate as the model chemotherapeutic agent and the drug loaded nanoparticles were then evaluated by in vitro and in vivo techniques to investigate their cellular toxicity and blood kinetics. We have also investigated their biodistribution profile in murine tumour models and imaged their tumour uptake by gamma scintigraphy post labeling with technetium-99m radioisotope (99mTc).



Polyethylene glycol diacrylate (PEGDA) (MW 575), Pentaerythritol tetraacrylare (PETRA) and Ethyleneglycol dimethacrylate(EGDMA) were procured from M/s Sigma Aldrich, USA. Azobis(isobutyro-nitrile)(AIBN) was procured from M/s SRL, Mumbai. Technetium-99m was procured from Regional Center for Radiopharmaceuticals (Northern region), Board of Radiation and Isotope Technology (BRIT), Department of Atomic Energy, India. Infrared spectra (IR) were recorded by the KBr pellet method in the range of 4000 – 400 cm−1 on a Perkin Elmer Spectrum BX-II spectrophotometer. NMR measurements were carried out on a Bruker 400 MHz system. Mass spectroscopic analysis was performed using an Agilent 1100 System coupled with LC operation in ESI (Electro Spray Ionization) positive/negative mode. UV-Vis scanning was done on a UV-Vis spectrophotometer, ECIL, India, as per reported literature [[24]]. Gamma ray spectrometer (type GRS23C)(Electronics Cooperation of India Pvt. Ltd., India, was used for determining the amount of activity (γ-emitter) in the samples. Gamma scintillation camera (HAWKEYE) was used for imaging of animals.

Animal models for biological evaluation

Balb/c mice of either sex (weighing 25-30 g) with no prior drug treatment were used for biodistribution studies and gamma imaging. Healthy, New Zealand Albino rabbits (2.5-3 Kg) were employed for blood kinetics studies. All animal experiments and study protocols were approved by the Committee for the Purpose of Control and Supervision of Experiments on Animals (CPCSEA), Government of India, New Delhi.

Normal Balb/c mice, each weighing about 25-30 g, were inoculated with Ehrlich Ascites Tumour (EAT). The EAT cells were maintained in the ascites form by serial weekly passage. Exponentially growing cells were harvested and 10 ×106 (approx) cells were injected subcutaneously in the right hind leg of the mice when a palpable tumour in the volume range of 0.9 ± 0.1 cm3 was observed in 7-10 days. Mice and rabbits were housed under conditions of controlled temperature of 22 ± 2°C and preserved on standard diet and water. All possible steps were taken to minimize the suffering of the animals at each stage of the experiment.

Synthesis of crosslinked nanoparticles by free radical thermal polymerization

The nanoparticles were prepared by free radical thermal polymerization using AIBN as a thermal initiator. The reaction was carried out in a 3-necked round bottom flask equipped with a condenser, thermometer, round bead and a nitrogen inlet. Required amounts of the polymer (PEGDA), solvent (DMF) and the desired crosslinkers, PETRA or EGDMA, were added to the round bottom flask as per Table 1, which was placed in the water bath. As soon as the temperature of the water bath reached 70°C, AIBN was added to the reaction mixture (Table 1), and continuously stirred at a constant temperature of 70°C for 12 h. A white product precipitated out on addition of excess of cold diethyl ether which was filtered using vacuum followed by thorough washing (2-3 times) with diethyl ether. The final product was air dried overnight before further evaluation. Using the nanoprecipitation technique, nanoparticles of these crosslinked systems were prepared after optimization of the polymer concentration so as to achieve the least particle size.

Table 1 Synthesis of crosslinked nanoparticles by free radical thermal polymerization

The drug loading of PP1 was carried out using MTX as a model drug in 1:10 drug:polymer ratio. The in vitro release profile was studied in PBS buffer (pH 7.4) and at pH 5.5 in acetate buffer. The percentage drug release was calculated using the equation:

% Drug released = 1 Absorbanc e t Absorbanc e t × 100 %

‘t’ being the time at which the absorbance is measured and ‘t0’ the initial time.

Characterization of nanoparticles

Dynamic light scattering measurements were used to obtain values of average hydrodynamic diameter in dilute dispersions at 25°C using a Malvern Zetasizer ZS 90 equipped with a He-Ne laser beam at a wavelength of 632.8 nm (scattering angle of 90°). Prior to analysis, solutions were filtered through a Millex filter (pore size ≈ 0.45 μm) to remove dust. The determination of diffusion coefficient was calculated by fitting the data with the cumulants method and diameters were estimated by the Stokes–Einstein equation, assuming a population of non-interactive spherical particles [[25]].

Cytotoxicity of nanoparticles

Cytotoxicity of the bare nanoformulations was determined using V79 fibroblast cells and the anticancer activity of the drug loaded formulation was assayed against MCF-7 breast cancer cells by the MTT {3-4,4-dimethylthiazole-2-yl)-2,5-diphenyl-2H-tetrazolium bromide} assay. Exponentially growing cells were plated in a 96-well microtitre plate at a uniform cell density of 10,000 cells/well, 24 h prior to treatment. Cells were treated with varying concentrations of the formulations (10-1000 μM) for different time intervals (12-72 h) and MTT assays were performed in triplicate. At the end of the treatment the treated cells were incubated with MTT at a final concentration of 0.5 mg/ml for 2 h at 37°C and the medium was removed. After specified time intervals (12,24,48, 72 h) the cells were lysed and the formazan crystals were dissolved using 150 μl of DMSO. Optical density was measured on 150 μl extracts at 570 nm (reference filter: 630 nm). Mitochondrial activity was expressed as percentage of viability compared to negative control. Percentage of viability = [OD(570 nm-630 nm)test product/OD(570 nm-630 nm)negative control] × 100.

Radiolabeling of nanoformulations

Both the drug loaded and unloaded formulations were labeled with 99mTc by the direct labeling method. Briefly, 100 μL of sterile sodium pertechnetate in saline (containing approx. 74-110 MBq of 99mTcO4 obtained by solvent extraction method from Molybdenum) was added to 100 μL (1 mg/mL) of each formulation followed by addition of 50 μL stannous chloride (2 mg/mL in 10% glacial acetic acid); pH was adjusted to 6.5 using 0.1 M NaOH, and the resulting solution was incubated at 37˚C for 15 mins. The labeled formulations, thus obtained, were stored in sterile shielded vials for subsequent studies. The radiolabeling efficiency was determined by ascending instant thin layer chromatography (ITLC) as reported in detail elsewhere [[26]].

In vitro human serum stability

The metabolic stability of the nanoformulations was ascertained in vitro in freshly collected human serum from healthy volunteers. Human serum was prepared by allowing blood collected from healthy human volunteers to clot for 1hr at 37°C in a humidified incubator maintained at 5% carbon dioxide, 95% air. The samples were then centrifuged at 400 g and the serum was filtered through a 0.22 μm filter into sterile plastic culture tubes. 100 μL of 99mTc labeled formulations were incubated respectively in 900 μL of this serum (in duplicate) at 37°C and analyzed to check for any dissociation of the complex by ITLC using silica gel strips and 0.9% NaCl aqueous solution (saline) as developing solvent. The change in labeling efficiency was monitored over a period of 24 hr.

In vivo evaluation

Blood clearance and plasma protein binding studies in rabbits

Blood clearance of 99mTc-labeled nanoformulations was studied in healthy New Zealand Albino rabbits weighing 2.5-3.5 kg (n = 3). 300 μL of the individual radiolabeled complexes (10 MBq) were administered intravenously through the dorsal ear vein. Blood samples were withdrawn from the other ear vein at different time intervals ranging from 5 mins-24 h. Persistence of activity in the circulation was calculated as percentage injected dose per whole blood, assuming total blood volume as 7% of the body weight. The radioactivity of the precipitate and supernatant was measured in a well-type gamma spectrometer.

Using the above blood samples, plasma was separated out by centrifugation, and the plasma proteins were precipitated by addition of 10% trichloroacetic acid (TCA). The radioactivity of the precipitate and supernatant was measured in a well-type gamma spectrometer.

Biodistribution in mice

Tumour bearing mice were administered 100 μL (3.7 MBq) of 99mTc labeled formulations, respectively, through the tail vein(i.v.). At 1, 2, 4 and 24 h post injection, the animals (n = 3) were euthanized and blood was collected by cardiac puncture into pre-weighed tubes. The mice were then dissected and different organs (heart, lungs, liver, spleen, kidneys, stomach, intestine, bone, muscle (normal and tumour) and brain) were removed, weighed and their radioactive counts taken with the help of a gamma counter. Uptake of the radiolabeled compound into each organ was measured per gram of the tissue/organ and expressed as percentage injected dose per gram organ weight. The radioactivity remaining in the tail (point of injection) was also measured and taken into account while calculating the radioactivity.

Gamma scintigraphy

The tumour bearing mice were administered 100 μl (3.7MBq) of 99mTc labeled formulations, respectively (i.v.), through the tail vein and gamma imaging was performed at different time intervals using a planar gamma camera equipped with a collimator.

Results and discussion

Several criteria including control over biological, chemical and physical properties are required for the design and development of an effective nanoparticle based drug carrier system for in vivo biomedical applications. These may include non-toxicity to cells, stability for prolonged circulation in blood stream, high loading efficiency and controllable release of therapeutics in addition to elimination of empty carrier after drug release. With this view, an effort was made to design a nanoparticulate system based on the biocompatible PEG matrix, using PEGDA, that contains crosslinkable sites in the polymer backbone. Crosslinked nanoparticles of polyethylene glycol were prepared by free radical polymerization and crosslinking of PEGDA chains with EGDMA and PETRA in the presence of AIBN. Owing to its ease of usage we opted for the free radical thermal polymerization technique using AIBN as the thermal initiator. The minimum and maximum concentrations for forming stable particles were ranging from 70-90% for EGDMA and PETRA. Use of crosslinkers lower than 70% resulted in incomplete crosslinking while concentrations greater than 90% led to precipitation.

IR spectroscopy was performed to confirm the formation of crosslinks between PEG and the crosslinking monomers. The IR spectra of the reactants (PEGDA, EGDMA, PETRA) and the product (PEGDA-based network) were compared for changes in vital peaks (Figure 1a,b). The FTIR spectra of PEGDA, EGDMA and PETRA had typical absorption bands of medium intensity at about 1640 cm−1 corresponding to alkenes. This band completely disappeared in the spectra of the networks owing to the consumption of – C = C – bonds during the crosslinking reaction. Also, the wavenumber of the carbonyl stretching resonance (C = O) of the acrylate moiety shifts from 1720 to 1730 cm−1 on reaction. These were corroborated by the NMR spectroscopy results. The 1H NMR spectra of the crosslinked structures showed a complete disappearance of the peaks in the 5.5 – 6.5 ppm region corresponding to acrylate terminal functionalities of PEGDA, EGDMA and PETRA. These results indicated that the – C = C – double bonds were successfully incorporated into the PEG based network.

Figure 1
figure 1

a: FTIR spectra of PEGDA, EGDMA and crosslinked PEGDA formulations (PE). b: FTIR spectra of PEGDA, PETRA and crosslinked PEGDA formulations (PP).

The average particle size of the prepared crosslinked nanoparticulate formulations was found to be in the range of 130 nm to 349 nm depending on the concentration and type of the polymeric system (Table 2). It was observed that the polymeric formulations prepared using PETRA crosslinker (PP series) were found to give relatively lower particle sizes than the ones prepared using the EGDMA crosslinker (PE series). Both the systems showed unimodal narrow particle size distributions with negative zeta potential values (Additional file 1: Figure S1 and Figure S2). The average particle size of the system consisting of EGDMA as a crosslinking agent was found to be in the range of 277 nm to 349 nm with varying concentration of the system while the particle size of the formulations varied from 130 nm to 211 nm when PETRA was used as the crosslinking agent. The zeta potential values hovered around -8 mV in the PE series whereas they varied from -13 to -21 mV in the PP series, a favorable aspect for in vivo applications. These results showed that as the number of the functional moiety, which is bulky acrylate group, increased from 2 to 4, the particle size of the formulations decreased by about 45-60%. This suggested that the number of the crosslinkable functional moieties strongly influences the formation of stable particles. Also, within the PE series, the particle size decreased with increasing concentration of polymer and crosslinker from PE1 to PE3, while in the PP series, the particle size increased from PP1 to PP3. That is, the smaller the number of the crosslinkable functional moieties in the crosslinking agent, the higher the concentration of crosslinking agent was needed for the formation of smaller particles. On the other hand, the larger the number of the crosslinkable functional moieties, the lower the concentration of it was needed. Similar results have been reported by other groups for the formation of crosslinked microspheres [[27]]. Based on these results PP1 was chosen as the model system for further drug loading experiments. But before that, it was imperative to check whether this carrier system was itself a source of toxicity to the in vivo system or not.

Table 2 Particle size and zeta potential measurements

The in vitro cytotoxicity studies of this system were done by the MTT assay. The formulation was tested for its ability to induce cytotoxicity in V79 fibroblast cells using an assay of mitochondrial activity (MTT assay). After 24, 48, and 72 h of exposure, viability was assessed on the basis of cellular conversion of MTT into a formazan product. A plot of percentage viability against the concentration revealed a decrease in the mitochondrial activity of the nanoformulation with increased concentration of upto 1000 μM (Figure 2). Even after 48 h of incubation, the formulations appeared to be non-toxic upto very high concentrations of almost 800 μM. These results suggested that the PETRA crosslinked nanoparticles of PEGDA are nontoxic to normal cells which confirmed their safety for non-cancerous cells. Of these PETRA crosslinked formulations, PP1, which formed the smallest size of nanoparticles, was taken as the matrix based system for further drug loading and biological evaluations. The anticancer activity of the free MTX and MTX loaded PP1 (M-PP1) was studied on MCF-7 breast cancer cells. MTT assay showed that both the free drug and the drug loaded nanoformulation could significantly suppress MCF-7 cell proliferation in a dose and time dependent manner (Figure 3a-c). While at the same concentration, the MTX loaded PP1 showed significantly higher inhibition rates against MCF-7 cells compared to free MTX especially at higher time points of 24 h and 48 h. In this the unloaded nanoformulation (U-PP1) was taken as the control and it was found to show negligible effect on cell viability (Figure 3). Thus the cytotoxicity of the MTX loaded nanoformulations was confirmed to be because of the encapsulated MTX.

Figure 2
figure 2

In vitro cytotoxicity of PETRA crosslinked PEGDA formulations; PP 1, PP 2 and PP 3 after 48 h of incubation.

Figure 3
figure 3

Anticancer activity of MTX loaded PP1 in MCF-7 cell line at (a) 12 h (b) 24 h (c) 48 h.

Polymeric nanoparticles can be loaded with drugs using three major strategies viz.-a-viz. covalent attachment of the drug to the particle surface or to the polymer prior to preparation, adsorption of the drug to a preformed carrier system, and incorporation of the drug into the particle matrix during particle preparation [[28]]. However, the important condition is that the bioactivity of therapeutic agents must remain intact during this preparation process. With this in view the crosslinked PEG network was used to encapsulate MTX. By optimization of the nanoprecipitation conditions our PEG based crosslinked matrix readily self assembled into reproducible polymeric micelles actively encapsulating the MTX particles in solution. The MTX loaded dispersions (MTX-PP1) displayed a yellow colour as compared to the almost translucent unloaded ones (Figure 4 inset). In order to study the in vitro release of the incorporated drug, membrane diffusion techniques are often used. In these cases, drug release follows more than one mechanism. In case of release from the surface of the nanoparticles, the adsorbed drug quickly dissolves on contact with the release medium. The entrapped drug then gets gradually released by the diffusion mechanism. Loading and release characteristics of methotrexate from these particles was studied at pH 5.5 and 7.4 using these membrane diffusion techniques. The unloaded drug and the organic solvent DMSO were removed by dialysis against distilled water. Drug loading content and drug loading efficiency was then determined spectrophotometrically at 303 nm. The MTX loaded PP1 was found to have a drug loading content of 7.68% and an encapsulation efficiency of 65.8%. The drug release profile of free MTX and MTX loaded polymeric nanoparticles over a 72 h study period is shown in Figure 4. Free MTX was completely released within 6 h at pH 5.5 and within 7 h at pH 7.4 while after encapsulation in the PEG based matrix the in vitro release pattern of MTX showed a drastic change and only 20-25% of the drug could be released from the matrix bound particles within the same duration. This clearly indicates the absence of any free unloaded MTX in the prepared polymeric particle solutions as no burst release effect could be seen. The release studies of the MTX-loaded particles indicate a biphasic release pattern, similar for both the pH conditions. Almost 40-50% of the drug was released from the particles within the first 24 h. Thereafter, a very slow drug release pattern was observed and a cumulative 50-65% MTX release was seen over a period of 72 h (the period of study) owing to the release of the entrapped drug by the diffusion mechanism. This could be an advantageous feature of this MTX-loaded polymeric system where initial fast drug release provides a higher dose followed by a controlled release during the rest of the duration of therapy.

Figure 4
figure 4

In vitro Drug release profile of free MTX and MTX loaded PETRA crosslinked PEGDA formulation over 72h.

PP1 and the MTX loaded PP1 formulations (MTX-PP1) were labeled with 99mTc. All the labeling parameters such as pH, concentration of reducing agents (SnCl2), temperature, etc. were standardized to achieve the maximum labeling efficiency [[29]]. The proteolytic degradation of the radiolabeled formulations was determined in human serum in vitro. ITLC analysis of the human serum revealed that the 99mTc-nanoformulations remained sufficiently stable during incubation at 37°C with human serum. A maximum of 8% of radioactivity degraded after 24 h of incubation advocating a high in vitro stability of almost 92% of the nanoformulation for upto 24 h.

A comparative evaluation of the blood clearance profile of the radiolabeled drug and nanoformulation in normal rabbits showed a biphasic mode of clearance (Figure 5). The radiolabeled drug, 99mTc-MTX demonstrated a quicker washout from the blood in a biphasic manner with a fast and slow half-life time of 35 mins and 17 h respectively, and only 25% of the injected dose remaining after 2 h of injection. However, the radiolabeled nanoformulation, 99mTc-MTX-PP1, exhibited relatively slower clearance in a somewhat biphasic pattern from blood circulation as expected for a matrix based system with almost 50% of the injected labeled compound remaining in blood 1 h post injection. The rest remained in circulation for upto 24 h and was gradually cleared from systemic circulation owing to the small size of the formulations and also perhaps not being readily taken up by the reticuloendothelial system (RES). 75-85% of the nanoparticulate carriers were eliminated from the blood circulation within 24 h. The t½ (fast) for the nanoformulation was found to be 45 mins, and the t½(slow) was 27.5 h respectively. At every time point the amount of the labeled MTX-PP1 conjugate in blood was more than the neat drug, thus suggesting longer blood retention, as also indicated by the half life-time values.

Figure 5
figure 5

Blood clearance profile of 99m Tc labeled MTX and PETRA crosslinked PEGDA formulation (PP1) over a period of 24 h.

Protein binding studies showed a difference in the plasma protein binding of 99mTc-MTX as compared to its encapsulated form. Binding of 99mTc-MTX to plasma proteins was only 68% whereas it was 54-58% in the case of 99mTc-MTX-PP1 nanoformulation probably because of the PEG based matrix.

Figure 6 represents complete tissue distribution after intravenous administration of 99mTc-labeled MTX-PP1 and results are expressed as percentage of the injected dose of 99mTc-labeled compounds accumulated per gram of tissue (%ID/g of tissue) at different time intervals. Biodistribution study of the drug loaded formulation in tumour bearing mice showed remarkable localization in tumour muscles (Figure 6) which could be well differentiated as compared to the negligible uptake in the normal muscles. This was also corroborated by the tumour-to-blood ratios that improved at increasing time points (Figure 7). A low uptake of radioactivity was observed in the stomach at all the time points(less than 2% ID/g) indicating a minimal in vivo decomposition of the radiolabeled nanoformulation to form the free 99mTcO4. The radiolabeled formulation accumulated to a higher level in the liver and kidneys at early time points after injection. The route of excretion of both the compounds was therefore perceived to be hepatobiliary. This clearly indicated that these crosslinked nanoparticulate carriers eventually get eliminated from the body.

Figure 6
figure 6

Biodistribution of MTX loaded PETRA crosslinked PEGDA formulation (PP1) over a period of 24 h.

Figure 7
figure 7

The relative tumour uptake of PETRA crosslinked PEGDA formulation (PP1) compared to the contralateral normal muscle (tumour:muscle ratio) over a period of 24 h.

The relative tumour uptake of the 99mTc labeled formulations compared to the contra-lateral normal muscle (tumour:muscle ratio) in balb/c mice is shown in Figure 7. The MTX loaded formulation showed high uptake in tumour muscles. This uptake helped to clearly delineate the tumour from the rest of the normal muscle which was also corroborated by the whole body tumour scintigraphic image shown in Figure 8.

Figure 8
figure 8

Whole-body γ-scintigraphic image of balb/c mice with subcutaneous EAT tumor above the right hind leg injected with 99m Tc labeled PETRA crosslinked PEGDA formulation.


Synthesis and characterization of the PEG based nanoparticles has been described in this study. These were successfully loaded with the anticancer drug, MTX, to evaluate their potential for anticancer drug delivery. The in vitro drug release pattern of the drug showing an initial fast release within the first 6 h followed by an eventual gradual release over 72 h could well be exploited for therapy regimes spread out over long durations thereby reducing the frequency of drug uptake. For clinical relevance, in addition to obtaining low non-specific uptake in healthy cells, sufficient uptake must occur in tumour cells to cause cell death. The MTT assay on fibroblast cells (healthy cells) and MCF-7 cells(human carcinoma) proved the clinical significance of these MTX loaded PETRA crosslinked PEGDA nanoparticles. The avid tumour uptake of the 99mTc-labeled nanoformulation and its gradual tumour washout demonstrated its use both as a tumour diagnostic agent as well as a therapeutic agent for cancer therapy. However, detailed studies on tumour proliferation rate and survival rates in animal models can give significant information on the therapeutic efficacy of these particles, which can form part of our future research work. Also, labeling of these crosslinking polymeric systems with gadolinium as an imaging marker can also form part of our future studies so imaging with MRI can be utilized. The investigations carried out as part of this work gave adequate evidence that the prepared crosslinked polymeric nanoparticulate formulations may be vital nanoparticulate carriers of chemotherapeutic drugs such as methotrexate, for potential drug delivery applications.

Additional file


  1. Koo AN, Lee HJ, Kim SE, Chang JH, Park C, Kim C, Park JH, Lee SC: Thermosensitive cross-linked polymer vesicles for controlled release system. New J Chem 2006, 30: 577-582. 10.1039/b516053g

    Article  Google Scholar 

  2. Colson YL, Grinstaff MW: Biologically responsive polymeric nanoparticles for drug delivery. Adv Mater 2012, 24: 3878-3886. 10.1002/adma.201200420

    Article  Google Scholar 

  3. Chan JM, Valencia PM, Zhang L, Langer R, Farokhzad OC: Polymeric nanoparticles for drug delivery. Methods Mol Biol 2010, 624: 163-175. 10.1007/978-1-60761-609-2_11

    Article  Google Scholar 

  4. Locatelli E, Franchini MC: Biodegradable PLGA- b -PEG polymeric nanoparticles: synthesis, properties, and nanomedical applications as drug delivery system. J Nanoparticle Res 2012, 14: 1316. 10.1007/s11051-012-1316-4

    Article  Google Scholar 

  5. Gauthier MA, Klok HA: Polymer-protein conjugates: an enzymatic perspective. Polym Chem 2010, 1: 1352-1373. 10.1039/c0py90001j

    Article  Google Scholar 

  6. Larson N, Ghandehari H: Polymeric conjugates for drug delivery. Chem Mater 2012,5(5):840-853. 13 10.1021/cm2031569

    Article  Google Scholar 

  7. Sanchis J, Canal F, Lucas R, Vicent MJ: Polymer–drug conjugates for novel molecular targets. Nanomedicine 2010,5(6):915-935. 10.2217/nnm.10.71

    Article  Google Scholar 

  8. Sun T, Jin Y, Qi R, Peng S, Fan B: Oxidation responsive mono-cleavable amphiphilic di-block polymer micelles labeled with a single diselenide. Polym Chem 2013,2013(4):4017-4023. 10.1039/c3py00406f

    Article  Google Scholar 

  9. Lysenko EA, Kulebyakina AI, Chelushkin PS, Rumyantsev AM, Kramarenko EY, Zezin AB: Polymer micelles with hydrophobic core and ionic amphiphilic corona. 1. statistical distribution of charged and nonpolar units in corona. Langmuir 2012,28(49):17108-17117. 10.1021/la3026039

    Article  Google Scholar 

  10. Rios-Doria J, Carie A, Costich T, Burke B, Skaff H, Panicucci R, Sill K: A versatile polymer micelle drug delivery system for encapsulation and in vivo stabilization of hydrophobic anticancer drugs. J Drug Deliv Artic ID 2012, 951741: 1-8. 10.1155/2012/951741

    Article  Google Scholar 

  11. Hu ZL, Qu X, Yang Z: pH-sensitive polymeric vesicles from coassembly of amphiphilic cholate grafted poly(L-lysine) and acid-cleavable polymer-drug conjugate. Langmuir 2012,28(33):11988-11996. 10.1021/la3015767

    Article  Google Scholar 

  12. Wang J, Yao K, Wang C, Tang C, Jiang X: Synthesis and drug delivery of novel amphiphilic block copolymers containing hydrophobic dehydroabietic moiety. J Mater Chem B 2013, 1: 2324-2332. 10.1039/c3tb20100g

    Article  Google Scholar 

  13. Oikawa Y, Lee S, Kim DH, Kang DH, Kim BS, Saito K, Sasaki S, Oishi Y, Shibasaki Y: One-pot synthesis of linear-hyperbranched amphiphilic block copolymers based on polyglycerol derivatives and their micelles. Biomacromolecules 2013,14(7):2171-2178. 10.1021/bm400275w

    Article  Google Scholar 

  14. Wang Y, Hong CY, Pan CY: Galactose-based amphiphilic block copolymers: synthesis, micellization, and bioapplication. Biomacromolecules 2013,14(5):1444-1451. 10.1021/bm4003078

    Article  Google Scholar 

  15. Vedha Hari BN, Kalaimagal K, Porkodi R, Gajula PK, Ajay JY: Dendrimer: globular nanostructured materials for drug delivery. Int J Pharm Tech Res 2012,4(1):432-451.

    Google Scholar 

  16. Liu J, Gray WD, Davis ME, Luo Y: Peptide- and saccharide-conjugated dendrimers for targeted drug delivery: a concise review. Interface Focus 2012, 2: 307-324. 10.1098/rsfs.2012.0009

    Article  Google Scholar 

  17. Wu X, Biatry B, Cazeneuve C, Guy RH: Drug delivery to the skin from sub-micron polymeric particle formulations: influence of particle size and polymer hydrophobicity. Pharm Res 2009,26(8):1995-2001. 10.1007/s11095-009-9915-1

    Article  Google Scholar 

  18. Roy K, Wang D, Hedley ML, Barman SP: Gene delivery with in-situ crosslinking polymer networks generates long-term systemic protein expression. Mol Ther 2003,7(3):401-408. 10.1016/S1525-0016(03)00008-X

    Article  Google Scholar 

  19. Zha L, Banik B, Alexis F: Stimulus responsive nanogels for drug delivery. Soft Matter 2011, 7: 5908. 10.1039/c0sm01307b

    Article  Google Scholar 

  20. Nisha Mary J, Pramod Kumar S: Cross-linked nanoparticles of cytarabine: encapsulation, storage and in-vitro release. Afr J Pharm Pharmacol 2007, 1: 010-013.

    Google Scholar 

  21. Debnath S, Datta D, Babu MN, Kumar RS, Senthil V: Studies on the preparation and evaluation of chitosan nanoparticles containing cytarabine. Int J Pharm Sci Nanotechnol 2010,3(2):ᅟ-ᅟ.

    Google Scholar 

  22. Xu P, Van Kirk EA, Li S, Murdoch WJ, Ren J, Hussain MD, Radosz M, Shen Y: Highly stable core-surface-crosslinked nanoparticles as cisplatin carriers for cancer chemotherapy. Colloid Surf B 2006, 42: 50-57. 10.1016/j.colsurfb.2006.01.004

    Article  Google Scholar 

  23. Peisheng X, Van Kirk EA, Murdoch WJ, Yihong Z, Isaak DD, Maciej R, Youqing S: Anticancer efficacies of cisplatin-releasing ph-responsive nanoparticles. Biomacromolecules 2006,7(3):829-835. 10.1021/bm050902y

    Article  Google Scholar 

  24. Kakkar D, Tiwari AK, Chuttani K, Kumar R, Mishra K, Singh H, Mishra AK: Pegylated isoniazid conjugate for reduced toxicity and sustained release. Ther Deliv 2011,2(2):205-212. 10.4155/tde.10.97

    Article  Google Scholar 

  25. Finsy R: Particle sizing by quasi-elastic light-scattering. Adv Colloid Interf Sci 1994, 52: 79-143. 10.1016/0001-8686(94)80041-3

    Article  Google Scholar 

  26. Kakkar D, Tiwari AK, Chuttani K, Khanna A, Datta A, Singh H, Mishra AK: Design, synthesis and antimycobacterial property of PEG-bis(INH) conjugates. Chem Biol Drug Des 2012,80(2):245-253. 10.1111/j.1747-0285.2012.01394.x

    Article  Google Scholar 

  27. Ha M, Lee K, Choe S: Crosslinkable functional moiety for the formation of highly crosslinked stable microspheres in the precipitation polymerization. Polymer 2008, 49: 4592-4601. 10.1016/j.polymer.2008.08.013

    Article  Google Scholar 

  28. Gardouh AR, Gad S, Ghonaim HM, Ghorab MM: Design and characterization of glyceryl monostearate solid lipid nanoparticles prepared by high shear homogenization. Br J Pharm Res 2013,3(3):326-346. 10.9734/BJPR/2013/2770

    Article  Google Scholar 

  29. Kakkar D, Tiwari AK, Chuttani K, Kaul A, Singh H, Mishra AK: Comparative evaluation of glutamate sensitive radiophramaceuticals: technetium-99m-glutamic acid and technetium-99m-diethylenetriaminepentaacetic acid-bis(glutamate) conjugate for tumour imaging. Cancer Biother Radiopharm 2010,25(6):645-655. 10.1089/cbr.2010.0848

    Article  Google Scholar 

  30. Deepa G, Thulasidasan AKT, Anto RJ, Pillai JJ, Kumar GSV: Cross-linked acrylic hydrogel for the controlled delivery of hydrophobic drugs in cancer therapy. Int J Nanomedicine 2012, 7: 4077-4088.

    Google Scholar 

  31. Buranachai T, Praphairaksit N, Muangsin N: Chitosan/Polyethylene glycol beads crosslinked with tripolyphosphate and glutaraldehyde for gastrointestinal drug delivery. AAPS PharmSciTech 2010,11(3):1128-1137. 10.1208/s12249-010-9483-z

    Article  Google Scholar 

  32. Koo AN, Lee HJ, Kim SE, Chang JH, Park C, Kim C, Park JH, Lee SC: Disulfide-cross-linked PEG-poly(amino acid)s copolymer micelles for glutathione-medited intracellular delivery. Chem Comm 2008, 48: 6570-6572. 10.1039/b815918a

    Article  Google Scholar 

  33. Wang K, Liu Y, Wen-Jie Y, Li C, Li Y, Zhuo R, Zhang X: Novel shell-crosslinked micelles with detachable PEG corona for glutathione-mediated intracellular drug delivery. Soft Matter 2013, 9: 692-699. 10.1039/c2sm27028e

    Article  Google Scholar 

  34. Zhang J, Men K, Gu Y, Wang X, Gou M, Gou G, Luo F, Qian Z: Preparation of core cross-linked PCL-PEG-PCL micelles for doxorubicin delivery in-vitro. J Nanosci Nanotechnol 2011,11(6):5054-5061. 10.1166/jnn.2011.4121

    Article  Google Scholar 

Download references


We thank Dr. R. P. Tripathi, Director INMAS, for providing necessary facilities for carrying out this research work. Financial assistance provided to SD by CSIR is duly acknowledged.

Author information

Authors and Affiliations


Corresponding authors

Correspondence to Dipti Kakkar Thukral or Anil K Mishra.

Additional information

Competing interest

The work was supported by Defence Research and Development Organization, Ministry of Defence, vide R&D project No. INM -311(3.1). The authors declare that they have no competing interests. No writing assistance was utilized in the production of this manuscript.

Authors’ contributions

DKT and AKM conceptualized the whole work, DKT drafted the manuscript. SD and SA carried out the synthesis and in vitro studies. KC carried out the technetium studies. All the authors have read and approved the final manuscript.

Electronic supplementary material


Additional file 1: Figure S1 and Figure S2. Gives details of the size and zeta potential measurements of EGDMA and PETRA crosslinked PEGDA formulations respectively. (PPTX 1 MB)

Authors’ original submitted files for images

Rights and permissions

Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (, which permits use, duplication, adaptation, distribution, and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Thukral, D.K., Dumoga, S., Arora, S. et al. Potential carriers of chemotherapeutic drugs: matrix based nanoparticulate polymeric systems. Cancer Nano 5, 3 (2014).

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI: